Manganese Oxide Nanoarchitectures as Broad-Spectrum Sorbents for Toxic Gases

ACS Appl Mater Interfaces. 2016 Jan 20;8(2):1184-93. doi: 10.1021/acsami.5b09508. Epub 2016 Jan 7.

Abstract

We demonstrate that sol-gel-derived manganese oxide (MnOx) nanoarchitectures exhibit broad-spectrum filtration activity for three chemically diverse toxic gases: NH3, SO2, and H2S. Manganese oxides are synthesized via the reaction of NaMnO4 and fumaric acid to form monolithic gels of disordered, mixed-valent Na-MnOx; incorporated Na(+) is readily exchanged for H(+) by subsequent acid rinsing to form a more crystalline H-MnOx phase. For both Na-MnOx and H-MnOx forms, controlled pore-fluid removal yields either densified, yet still mesoporous, xerogels or low-density aerogels (prepared by drying from supercritical CO2). The performance of these MnOx nanoarchitectures as filtration media is assessed using dynamic-challenge microbreakthrough protocols. We observe technologically relevant sorption capacities under both dry conditions and wet (80% relative humidity) for each of the three toxic industrial chemicals investigated. The Na-MnOx xerogels and aerogels provide optimal performance with the aerogel exhibiting maximum sorption capacities of 39, 200, and 680 mg g(-1) for NH3, SO2, and H2S, respectively. Postbreakthrough characterization using X-ray photoelectron spectroscopy (XPS) and diffuse-reflectance infrared Fourier transform spectroscopy (DRIFTS) confirms that NH3 is captured and partially protonated within the MnOx structure, while SO2 undergoes oxidation by the redox-active oxide to form adsorbed sulfate at the MnOx surface. Hydrogen sulfide is also oxidized to form a combination of sulfate and sulfur/polysulfide products, concomitant with a decrease in the average Mn oxidation state from 3.43 to 2.94 and generation of a MnOOH phase.

Keywords: air filtration; ammonia; hydrogen sulfide; manganese oxide; sulfur dioxide.

Publication types

  • Research Support, Non-U.S. Gov't
  • Research Support, U.S. Gov't, Non-P.H.S.