The toxicity characteristic leaching procedure (TCLP) is a regulatory testing method widely employed to evaluate the environmental friendliness of waste materials. TCLP analysis provides a fast, easy and economical way to determine the mobility of waste pollutants under simulated landfill conditions. Recent studies on metal stabilization have reported the potential for nickel and copper aluminates to form in thermal treatment conditions, and suggested a more reliable method of stabilizing hazardous metals, particularly when products are to be reused. There is thus an urgent need for a convenient and effective method of quantifying metal leachability and identifying the metal leaching behavior of sparingly soluble materials. In this study, standard TCLP analysis was modified into a prolonged leaching experiment to investigate the leaching behavior of nickel and copper oxides (NiO and CuO) and their aluminates (NiAl(2)O(4), CuAl(2)O(4) and CuAlO(2)). The results demonstrate the difficulty of differentiating the leachability of highly insoluble phases, such as NiO and NiAl(2)O(4), using the standard TCLP. The prolonged TCLP method, however, confirmed NiAl(2)O(4) to have a lower degree of intrinsic leachability than NiO and that it could be expected to undergo congruent dissolution under landfill conditions. For the more soluble copper system, the aluminates were still found to possess a much lower degree of leachability, and their leaching behavior to follow an incongruent dissolution pattern. The results of this study prove prolonged TCLP analysis to be a convenient and effective way to evaluate the environmental friendliness of metal waste and to identify the leaching behavior of waste materials.