Objectives: To measure the shear punch strength of eight resin-containing luting cements before and after immersion in acidic solution and ethanol at different temperatures (37 degrees C and 60 degrees C).
Method: Specimens were prepared from six resin luting cements; Set (SDI), Panavia F (Kuraray), RelyX Veneer (3M/ESPE), VarioloinkII (Ivoclar), Maxcem (Kerr), Nexus2 (Kerr) and two Resin-modified glass-ionomer luting cements (RM-GICs); GC Fuji Plus (GC Corporation), RelyX Luting 2 (3M/ESPE). For each material a total of 114 disc-shaped specimens were prepared. Six specimens were immersed in distilled water for 24 h at 37 degrees C, polished and subjected to baseline measurement for shear punch strength. The remaining 108 specimens were randomly divided into 18 groups of six, and immersed in three solutions; distilled water, 0.01 mol/L lactic acid, and 50% ethanol at 37 degrees C or 60 degrees C, for 1 week, 1 month or 3 months. Specimens were washed, dried and tested for final shear punch strength.
Results: Values were material and solution dependent. Values of Nexus 2 and Rely X Veneer are the highest, and Rely X Luting 2 the lowest. Ethanol and lactic acid specimens showed significantly lower values compared with the distilled water specimens.
Conclusion: The shear punch strengths of the resin-containing luting cements were affected by time and storage solution. While some of the resin luting cements had significantly higher values compared to that of the RM-GICs, there were no significant differences between the RM-GICs and resin cements such as Panavia F and Set.
Copyright 2010 Elsevier Ltd. All rights reserved.